Flash Annealing of Silver Coatings

ABSTRACT

Methods of processing coated articles, such as transparencies, are provided comprising flash annealing one or more layers of the coated article. The one or more layers may be reflective metallic layers, such as silver layers, or comprise a transparent conductive oxide, such as indium tin oxide, or a semiconductor.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional of U.S. patent application Ser. No.15/669,133, filed Aug. 4, 2017, which is hereby incorporated in itsentirety by reference.

BACKGROUND OF THE INVENTION Field of the Invention

Provided herein are methods of flash annealing coatings for articlesincluding transparencies and optical devices.

Technical Considerations

Transparent conductive oxides (TCOs) are often used in production ofarchitectural and automotive transparencies, as a dielectric layer, aswell as in electro-optical devices, such as light-emitting diodes(LEDs), for example organic LEDs (OLEDs), and solar cells, such asphotovoltaic thin film solar cells. LEDs and OLEDs are devices having anemissive layer that emits electromagnetic radiation, such as visiblelight, in response to the application of an electric current. Theemissive layer is located between two electrodes (an anode and acathode). When electric current is passed between the anode and thecathode (i.e., through the emissive layer), the emissive layer emitselectromagnetic energy. OLEDs are used in numerous applications, such astelevision screens, computer monitors, mobile phones, personal digitalassistants (PDAs), watches, lighting, and various other electronicdevices. U.S. Pat. No. 9,627,652 describes OLED devices. Due to theversatility of TCOs in architectural, optical, and optoelectronics,having a method of rapidly and inexpensively producing unique physical,e.g., electrical and/or optical, attributes in a TCO or semiconductorlayer is most desirable.

Solar control coatings are known in the fields of architectural andautomotive transparencies. Those coatings block or filter selectedranges of electromagnetic radiation, such as in the range of solarinfrared or solar ultraviolet radiation, to reduce the amount of solarenergy entering the vehicle or building. This reduction of solar energytransmittance helps reduce the load on the cooling units of the vehicleor building. In automotive applications, the transparency (such as awindshield) is typically required to have a relatively high visiblelight transmittance, such as greater than 70 percent, to allowpassengers to see out of the vehicle. For architectural applications,the visible light transmittance can be lower. In some architecturalapplications, it may be desirable to have a reflective outer surface soas to decrease visibility into the building to retain as much privacy aspossible, while still allowing visible light to enter the building andalso allowing the workers inside the building to see out.

As will be appreciated by one skilled in the architectural art, glass isused typically in either a tempered form or a non-tempered (annealed)form, depending upon the desired final use of the glass. For annealedglass, the glass is heated to the annealing point of the glass and thenallowed to slowly cool to below the strain point of the glass. Theannealed glass can be cut to desired final dimensions, such as for adoor, window, and the like. For even stronger glass, tempering is used.In tempering, glass is heated above the annealing point of the glass andthen rapidly cooled, such as by directing a cooling medium at the glass,to provide the glass with an exterior compressive force and an interiortensile force. Tempered glass is much stronger than annealed glass andis used where safety is an important factor. However, unlike annealedglass, tempered glass cannot be cut or it will shatter. Therefore, wheretempered glass is desired, the glass must be cut to the desired finaldimensions before tempering.

A conventional building may require both annealed (non-tempered) andtempered glass pieces with solar control coatings. For example, annealedglass with a solar control coating may be used on the lower floors whiletempered glass with a solar control coating is used on the upper floorsfor increased safety. Both the coated annealed glass and the coatedtempered glass should have the same or very similar opticalcharacteristics so that the building maintains the same overallaesthetic appearance. This causes a problem for coated glassmanufacturers. Tempering the coated glass pieces can result in thetempered products having different color or optical characteristics thanthe original annealed products due to changes in the coating caused bythe extra heating and rapid cooling steps required to temper the glass.This difference in color or other optical properties, such astransmittance or reflectance, between the coated tempered glass and thecoated annealed glass is not desirable if the annealed and temperedproducts are to be used in the same building.

Matching glass aesthetics is difficult. As a consequence, it would bedesirable to have a method of treating coated glass sheets in a mannerthat alters aesthetics of the glass to match that of tempered glasssheets, permitting two types of glass to be used in the same buildingwithout significant differences in aesthetics between the two types ofglass.

SUMMARY OF THE INVENTION

According to one aspect of the invention, a method of producing a coatedtransparency is provided. The method comprises depositing a stack ofthin layers on a transparent substrate, the stack comprising a firstdielectric layer over at least a portion of the substrate; a firstdiscontinuous metal layer over at least a portion of the firstdielectric layer; and a first primer layer over at least a portion ofthe first discontinuous metal layer; and flashing the transparency at atemperature ranging from 10° C. to 50° C. or ranging from 20° C. to 30°C., with a single flash of non-coherent light in the visible spectrumwith an intensity ranging from 1 J/cm2 to 7 J/cm2 for a pulse length ofup to 10 ms, thereby increasing visible light transmittance of thetransparency.

According to another aspect of the invention, a method of flashannealing a transparency is provided wherein, the transparencycomprises: a transparent substrate, a first dielectric layer over atleast a portion of the substrate, a first continuous metal layer over atleast a portion of the first dielectric layer, a first primer layer overat least a portion of the first metal layer, a second dielectric layerover at least a portion of the first primer layer, a second continuousmetal layer over at least a portion of the second dielectric layer, anda second primer over at least a portion of the second metal layer,comprising, flashing the transparency at a temperature ranging from 10°C. to 50° C. or ranging from 20° C. to 30° C., with a flash ofnon-coherent light in the visible spectrum with an intensity rangingfrom 1 J/cm² to 7 J/cm² for a pulse length of up to 10 ms, therebyincreasing visible light transmittance or decreasing emissivity of thetransparency.

According to yet another aspect of the invention, a non-temperedtransparency is provided, the method comprises

-   -   a. a float glass substrate;    -   b. a first dielectric layer over at least a portion of the glass        substrate;    -   c. a first silver layer over at least a portion of the first        dielectric layer;    -   d. a first titanium layer over at least a portion of the first        silver layer and having a thickness ranging from 1 to 2 nm;    -   e. a second dielectric layer over at least a portion of the        first titanium layer;    -   f. a second silver layer over at least a portion of the second        dielectric layer;    -   g. a second titanium layer over at least a portion of the second        silver layer and having a thickness ranging from 1 to 2 nm; a        first dielectric layer over at least a portion of the glass        substrate;    -   h. a third dielectric layer over at least a portion of the        second titanium layer;    -   i. a third silver layer over at least a portion of the third        dielectric layer;    -   j. a third titanium layer over at least a portion of the third        silver layer and having a thickness ranging from 1 to 2 nm; a        first dielectric layer over at least a portion of the glass        substrate;    -   k. a fourth dielectric layer over at least a portion of the        third titanium layer; and    -   l. a protective coating over at least a portion of the fourth        dielectric layer,    -   wherein the transparency has a CIELAB L*a*b* value of L* ranging        from 87 to 89, a* ranging from −3 to −5, and b* ranging from 3        to 5.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be described with reference to the following drawingfigures wherein like reference numbers identify like parts throughout.Unless indicated otherwise, layers and element depicted in the drawingfigures are not to scale and are depicted in a manner that facilitatesdescription of the elements and the structure of the depicted items.

FIG. 1 depicts a cross section of an article comprising a substrate anda partially flash annealed layer over the substrate.

FIG. 2 depicts a portion of an insulating glass unit.

FIG. 3 depicts a coated transparency comprising a discontinuous metallayer.

FIG. 4 depicts a portion of a discontinuous metal layer, for example asdescribed in relation to FIG. 3.

FIG. 5 depicts a coated glass article having one or more reflectivemetallic layers.

FIG. 6 depicts a coated glass article having three reflective metalliclayers.

FIG. 7 depicts schematically a method of patterning an article by aflash annealing method as described herein.

FIG. 8 provides a graph showing variation of sheet resistance as afunction of thickness for various ITO layer thicknesses.

FIG. 9 Provides a graph showing variation of emissivity as a function ofthickness for various ITO layer thicknesses.

FIGS. 10A and 10B provide Hall measurements, carrier concentration (FIG.10A) and mobility (FIG. 10B) for ITO layers of varying thicknessdeposited at 3 mTorr with 2.5% (% volume) oxygen or 4 mTorr with 1.5%oxygen.

FIGS. 11A and 11B provide graphs showing optical properties of flashannealed ITO layers having differing amounts of oxygen. FIG. 11A showstransmission (%) spectra, and FIG. 11B shows normalized absorptionspectra.

FIG. 12 provides a graph showing optical and electrical properties ofITO layers of varying thicknesses.

FIG. 13A shows the absorption coefficient spectrum for three samples ofITO-coated float glass where the ITO has different absorption spectra.FIG. 13B provides XRD traces for the same samples.

FIG. 14 shows XRD traces for four TCO layers with the same absorptioncoefficient, but different thicknesses as indicated before (BF) andafter (AF) flash treatment.

FIG. 15 provides a table of flash voltage conditions and sheetresistance measurements for Example 7.

FIG. 16 provides a table showing color and visible luminosity of asimulated insulated glass using coating properties as described inExample 7.

FIG. 17 provides selected center-of-glass performance characteristics ofa simulated insulated glass using coating properties as described inExample 7.

FIG. 18 is a graph comparing various samples as described in Example 8.

FIG. 19 is a graph comparing calculated adjustments to silver depositionconditions to achieve a target color match.

FIG. 20 is a graph comparing reduction in ΔE_(cmc) for a tested sampleas compared to SOLARBAN® 70XL on STARPHIRE®.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

As used herein, spatial or directional terms, such as “left”, “right”,“inner”, “outer”, “above”, “below”, and the like, relate to theinvention as it is shown in the drawing figures. However, it is to beunderstood that the invention can assume various alternativeorientations and, accordingly, such terms are not to be considered aslimiting. Further, as used herein, all numbers expressing dimensions,physical characteristics, processing parameters, quantities ofingredients, reaction conditions, and the like, used in thespecification and claims are to be understood as being modified in allinstances by the term “about”. Accordingly, unless indicated to thecontrary, the numerical values set forth in the following specificationand claims may vary depending upon the desired properties sought to beobtained by the present invention. At the very least, and not as anattempt to limit the application of the doctrine of equivalents to thescope of the claims, each numerical value should at least be construedin light of the number of reported significant digits and by applyingordinary rounding techniques. Moreover, all ranges disclosed herein areto be understood to encompass the beginning and ending range values andany and all subranges subsumed therein. For example, a stated range of“1 to 10” should be considered to include any and all subranges between(and inclusive of) the minimum value of 1 and the maximum value of 10;that is, all subranges beginning with a minimum value of 1 or more andending with a maximum value of 10 or less, e.g., 1 to 3.3, 4.7 to 7.5,5.5 to 10, and the like. Additionally, all documents, such as, but notlimited to, issued patents and patent applications, referred to hereinare to be considered to be “incorporated by reference” in theirentirety.

Further, as used herein, the terms “formed over”, “deposited over”, or“provided over” mean formed, deposited, or provided on but notnecessarily in contact with the surface. For example, a coating layer“formed over” a substrate does not preclude the presence of one or moreother coating layers or films of the same or different compositionlocated between the formed coating layer and the substrate. Likewise,the terms “under” or “between” in the context of specified coatinglayers does not preclude the presence of one or more other coatinglayers or films of the same or different composition located between therecited layers.

As used herein, the terms “polymer” or “polymeric” include oligomers,homopolymers, copolymers, and terpolymers, e.g., polymers formed fromtwo or more types of monomers or polymers, and a “plastic” is apolymer-containing material that optionally can contain additionaladditives to alter a property of the material.

The terms “visible region” or “visible light” refer to electromagneticradiation having a wavelength in the range of 380 nm to 800 nm. Theterms “infrared region” or “infrared radiation” refer to electromagneticradiation having a wavelength in the range of greater than 800 nm to100,000 nm. The terms “ultraviolet region” or “ultraviolet radiation”mean electromagnetic energy having a wavelength in the range of 300 nmto less than 380 nm. By “transparent” is meant having visible lighttransmission of greater than 0% up to 100%. By “translucent” is meantallowing electromagnetic energy (e.g., visible light) to pass throughbut diffusing this energy such that objects on the side opposite theviewer are not clearly visible. Although a typical “transparency” canhave sufficient visible light transmission such that materials can beviewed through the transparency, a “transparency” need not betransparent to visible light but may be translucent or opaque.

As used herein, the term “film” refers to a coating region of a desiredor selected coating composition. A “layer” can comprise one or more“films”, and a “coating” or “coating stack” can comprise one or more“layers”. The term “asymmetrical reflectivity” means that the visiblelight reflectance of the coating from one side is different than that ofthe coating from the opposite side. The term “critical thickness” meansa thickness above which a coating material forms a continuous,uninterrupted layer and below which the coating material formsdiscontinuous regions or islands of the coating material rather than acontinuous layer. The term “subcritical thickness” means a thicknessbelow the critical thickness such that the coating material formsisolated, non-connected regions of the coating material. The term“islanded” means that the coating material is not a continuous layerbut, rather, that the material is deposited to form isolated regions orislands.

Provided herein are methods of improving one or more physical attributesof a coated article or a coating layer of a coated article, as are foundin coated objects or transparencies, such as are found in architecturalglass, vehicle transparencies, light-emitting diodes (LEDs), organicLEDs, photovoltaic cells, electro-optic devices, etc. In aspects, thedescribed coated articles are useful in bottom-emitting or top-emittingLED or OLED devices, solar cells, such as photovoltaic thin film solarcells. For example, an LED or OLED may use at least one transparentconductive oxide as an electrode, through which light passes and isextracted from the emissive layer. TCOs for use as an electrode for anLED device should have low sheet resistance. It is to be understood thatthe methods and articles described herein are not limited to such uses.Therefore, it is to be understood that the specifically disclosedexemplary embodiments are presented simply to explain the generalconcepts of the invention, and that the invention is not limited tothese specific examples.

Flash annealing is a process by which an article comprising at least onelayer over a substrate is flashed with one or more pulses of visiblelight, resulting in a physical transformation of the one or more layersby the flash of visible light. Any source of visible light that canproduce a flash of sufficient luminous flux (energy time⁻¹) to flashanneal an article within the context of the present disclosure may beused in the methods described herein. The methods may utilize a broadspectrum flash, such as a xenon lamp flash, ranging from 1-10.0 J/cm²,and increments therebetween, for example from 3.5-6.0 J/cm², andpreferably from 4.0 to 5.0 J/cm². in aspects, the pulse length rangesfrom 0.1 ms to 10 ms, and increments therebetween, from 0.2 ms to 2 ms,and increments therebetween, for example from 250 μs to 1 ms, 500 μs,650 μs, 670 μs. Excessive flash energy will damage the targeted layer.Lamps useful for generating flashes include gaseous discharge lamps,such as helium or xenon lamps, and metal vapor lamps, such as mercuryvapor lamp. Multi-vapor discharge lamps may be used to achieve a moreuniform spectral distribution. In one aspect, the lamp is a xenondischarge flash lamp. In various aspects of the invention, a singleflash is capable of sufficiently modifying one or more physicalqualities of a layer. A “single flash pulse” includes: exposure of thetransparency or a portion thereof to one pulse; two or more pulsesflashing different portions of the transparency, or two or moreoverlapping pulses where each pulse of the overlapping pulses flashes adifferent area or portion of the transparency, but the two portionsflash one or more overlapping points on the surface of the transparency.

The articles described herein are coated and otherwise processed byconventional methods and systems, e.g., by an in-line magnetron sputterdeposition system. Articles can be conveyed into and from variousdeposition systems or treatment stations by conventional conveyingmethods and systems. Flashing of the articles can be performed at roomtemperature, typically in the range of from 20° C. to 30° C., such as at22° C. or 25° C., though flashing can be performed at temperaturesoutside this range, such as from 15° C. to 50° C. In aspects, one ormore flashtubes are placed in position over a conveyor and at a suitabledistance from the conveyor for flashing the article at a desirableintensity. A conveyor system moves the article relative to theflashtube(s), and timing of conveyor movement can be coordinated, e.g.,by computer control, with flashing of the article such that one or moreflashes are applied to any given position on the article. For largerarticles, multiple flashes can be used to flash all positions on thesurface of the article, and the flashes may overlap or abut each-otherso that the surface of the article is flashed with a sufficient amountof light to transform one or more physical attributes of the article, asdescribed herein, such as, without limitation: sheet resistance,emissivity, conductance, color, or transmittance.

In the methods and articles described herein, a substrate is coated withat least on layer that is flash annealed. Exemplary substrates includetransparent or opaque substrates, such as substrates comprising, withoutlimitation, glass, plastic, crystal, metal, ceramic, or combinationsthereof. Non-limiting examples of glass that can be used as a substrateinclude clear glass, Starphire®, Solargreen®, Solextra®, GL-20®, GL35™,Solarbronze®, Solargray® glass, Pacifica® glass, SolarBlue® glass,Solarphire® glass, Solarphire PV® glass, and Optiblue® glass, allcommercially available from PPG Industries Inc. of Pittsburgh, Pa. Forexample, glasses can include conventional soda-lime-silicate glass,borosilicate glass, or leaded glass. The glass can be clear glass. By“clear glass” is meant non-tinted or non-colored glass. Alternatively,the glass can be tinted or otherwise colored glass. The glass can beannealed or heat-treated glass. As used herein, the term “heat treated”means tempered or at least partially tempered. The glass can be of anytype, such as conventional float glass, and can be of any compositionhaving any optical properties, e.g., any value of visible transmission,ultraviolet transmission, infrared transmission, and/or total solarenergy transmission. By “float glass” is meant glass formed by aconventional float process in which molten glass is deposited onto amolten metal bath and controllably cooled to form a float glass ribbon.Examples of float glass processes are disclosed in U.S. Pat. Nos.4,466,562 and 4,671,155. As used herein, the term “solar controlcoating” refers to a coating comprised of one or more layers or filmsthat affect the solar properties of the coated article, such as, but notlimited to, the amount of solar radiation, for example, visible,infrared, or ultraviolet radiation, reflected from, absorbed by, orpassing through the coated article; shading coefficient; emissivity,etc.

Examples of additional suitable substrate materials include, but are notlimited to, plastic substrates, such as acrylic polymers, such aspolyacrylates; polyalkylmethacrylates, such as polymethylmethacrylates,polyethylmethacrylates, polypropylmethacrylates, and the like;polyurethanes; polycarbonates; polyalkylterephthalates, such aspolyethyleneterephthalate (PET), polypropyleneterephthalates,polybutyleneterephthalates, and the like; polysiloxane-containingpolymers; or copolymers of any monomers for preparing these, or anymixtures thereof; ceramic substrates; glass substrates; or mixtures orcombinations of any of the above.

Layers applied over the substrate often comprise metals, oxides,semiconductors, and dielectrics, including transparent metals, metaloxides, conductive oxides, semiconductors, and dielectrics. Physicalproperties or physical attributes include: transmittance; absorption;color; emissivity; sheet resistance; conductance, e.g., carrierconcentration or carrier mobility; crystallinity or crystal structure;refraction coefficient; or surface plasmon resonance, among othereffects, alone or in combination. Additional layers can includeprotective or overcoat layers, such as silica or aluminum silica layersas are broadly-known, for example as further described below in thecontext of various aspects of the disclosure.

Coating layers as described herein can be deposited by any conventionalmethod, such as, but not limited to, conventional chemical vapordeposition (CVD) and/or physical vapor deposition (PVD) methods.Examples of PVD processes include thermal or electron beam evaporationand vacuum sputtering (such as magnetron sputter vapor deposition(MSVD)). Other coating methods could also be used, such as, but notlimited to, sol-gel deposition. In one aspect, the coating can bedeposited by MSVD. Examples of MSVD coating devices and methods will bewell understood by one of ordinary skill in the art and are described,for example, in U.S. Pat. Nos. 4,379,040; 4,861,669; 4,898,789;4,898,790; 4,900,633; 4,920,006; 4,938,857; 5,328,768; and 5,492,750.

According to one aspect, a method of producing a coated substratecomprising a layer of a transparent conductive oxide or a semiconductoris provided. Non-limiting examples of transparent conductive oxidesinclude: oxides of titanium, hafnium, zirconium, niobium, zinc, bismuth,lead, indium, tin, and mixtures thereof, and may be doped with otherelements, such as gallium or aluminum. Specific examples of transparentconductive oxides include, without limitation: indium tin oxide, indiumzinc oxide, fluorinated tin oxide (“FTO”), a doped zinc oxide, such asgallium-, aluminum-, or tin-doped zinc oxide (“GZO”, “AZO” and “TZO”,respectively), or a doped titanium dioxide, such as niobium-doped TiO₂(“NTO”). Suitable transparent conductive oxides include oxygen-deficienttransparent conductive oxides. By “oxygen-deficient transparentconductive oxide”, it is meant that the conductive oxide is depositedunder conditions, such as by sputtering, e.g. by MSVD, in an inertatmosphere, such as an argon atmosphere with a subsaturation amount ofoxygen, yielding the oxygen-deficient, or sub-stoichiometric TCO.Oxygen-deficient TCOs, such as oxygen-deficient ITO, are broadly-knownand are readily made by those of ordinary skill in the art. As usedherein a recited percent of oxygen in a sputtering atmosphere refers tovolume percent. Non-limiting examples of semiconductors that may beflash annealed according to the methods described herein include: as anexample the flash annealing of amorphous silicon layers to producepolycrystalline Silicon and germanium films.

The method further comprises depositing over at least a portion of asubstrate in an inert atmosphere a transparent metal oxide orsemiconductor layer having an absorption coefficient at a wavelength inthe visible spectrum of at least 1,000 cm⁻¹; and flashing at least aportion of the transparent conductive oxide or semiconductor layer at atemperature ranging from 15° C. to 50° C., or ranging from 20° C. to 30°C., with a pulse energy ranging from 3.5 J/cm² to 6.0 J/cm², ofnon-coherent light within the visible spectrum that includes light thewavelength in the visible spectrum at which the layer has an absorptioncoefficient of at least 1,000 cm⁻¹. In one aspect, the pulse is a singlepulse, which is sufficient to, e.g., substantially decrease sheetresistance, increase conductance, decrease emissivity, and increasetransmittance of the layer and the article as a whole. In one aspect,the transparent metal oxide or semiconductor layer is a transparentconductive oxide layer, and in one aspect is an indium tin oxide layer,or an oxygen-deficient indium tin oxide layer having a thickness rangingfrom 200 to 400 nm, or 200 to 300 nm, for example 250 nm.

One feature of transparent conductive oxides, such as ITO, andsemiconductors that find use as coatings, e.g. on transparent substratesis that they have an absorption coefficient that can be optimized ormodified. For example, oxygen-deficient transparent conductive oxides,such as oxygen-deficient indium tin oxide as an example, has asufficiently large absorption coefficient at certain wavelengths suchthat light at those wavelengths cannot fully penetrate the completethickness of a layer of that material to permit flash annealing throughthe entire thickness of the layer. Thus, sufficient matching ofabsorption coefficient and thickness of a layer with lamp dischargespectrum and intensity such that the penetration depth of the lightproduced by the lamp that is capable of flash annealing the layer doesnot fully penetrate the full thickness of the layer will result in asplit or bifurcated layer with different physical attributes of theflashed portion of the layer as compared to the un-flashed portion ofthe layer to which light did not penetrate to a sufficient extent. Asuitable thickness for an indium tin oxide layer or an oxygen-deficientindium tin oxide layer at which the penetration depth of a Xenon lamppulse is less than the thickness of the layer is greater than 300 nm,for example ranging from 300 nm to 2 μm (microns) in thickness.

Referring to FIG. 1, and in the context of a transparent article 30, afirst layer 40 comprising a transparent conductive oxide orsemiconductor is deposited over a substrate 50. When flashed asdescribed herein, the first layer 40 is split into a first sub-layer 42and a second sub-layer 44 joined at a transition 46. The first sub layer42 of a transparent conductive oxide or semiconductor has a firstphysical state, for example and without limitation having a first sheetresistance, conductance, color, or transmittance, and the secondsub-layer 44 is converted by a light flash to a second physical state,for example and without limitation having a second sheet resistance,conductance, color, or transmittance. The first and second sub-layers 42and 44 can therefore be considered a single, integrated layer thatincludes the bottom sub-layer (distal to the flash) that remains in anunflashed state, and a top sub-layer immediately over the firstsub-layer that is converted by the light flash. By the nature of theflashing, the top and bottom sub-layers may be joined at the transition46 of unspecified thickness that has physical characteristics that maybe different from the first and/or second sub-layers, for example,intermediate to the first and second sublayers. An optional protectivelayer 60 is depicted. Additional layers may be included over or betweendepicted layers.

Traditional heating methods are incapable of forming a split transparentconductive oxide or semiconductor layer as is produced by the flashmethods described herein. Use of conductive heat requires raising thetemperature of the transparent conductive oxide or semiconductor layerto a temperature exceeding 400° C., and for thin layers, e.g. withthicknesses of less than 5 μm, and especially submicron thicknesses,such as in the range of the TCO layers described herein, the surfaceheat of the layer conducts through the entire layer essentiallyimmediately, resulting in a uniform transformation of the layerthroughout its thickness. Therefore, by flashing a layer having anappropriately high coefficient of absorption such that the light doesnot penetrate through the entire thickness of the layer, only theportion of the layer that the light penetrates will be transformed,leaving an untransformed layer. Such a configuration is useful tocontrol, e.g., color, transmittance, light scattering, light trapping,sheet resistance, reflectance, refraction, conductance, or otherrelevant physical parameters of a coated article.

According to another aspect of the disclosure, a method of flashannealing transparencies comprising metallic reflective layers isprovided. In one aspect, the method permits effective annealing oftransparencies comprising two or more metal, e.g. silver, layers. Theflash annealing facilitates close color matching of annealed productswith tempered products, decreased sheet resistance, increasedtransmittance, production of desirable color profiles, and a generalincrease in the quality of the product.

According to various aspects, coatings produced by the flash annealingmethod described herein may be used in an architectural transparency. Asan example, a non-limiting example of a transparency 10 incorporating athird surface coating, such as a coating comprising two or more silverlayers is illustrated in FIG. 2. The transparency 10 can have anydesired visible light, infrared radiation, or ultraviolet radiationtransmission and/or reflection. For example, the transparency 10 canhave a visible light transmittance of any desired amount, e.g., greaterthan 0% up to 100%.

The exemplary transparency 10 of FIG. 2 is in the form of a conventionalinsulating glass unit and includes a first ply 12 with a first majorsurface 14 (No. 1 surface) and an opposed second major surface 16 (No. 2surface). In the illustrated non-limiting aspect, the first majorsurface 14 faces the building exterior, i.e., is an outer major surface,and the second major surface 16 faces the interior of the building. Thetransparency 10 also includes a second ply 18 having an outer (first)major surface 20 (No. 3 surface) and an inner (second) major surface 22(No. 4 surface) and spaced from the first ply 12. This numbering of theply surfaces is in keeping with conventional practice in thefenestration art. The first and second plies 12, 18 can be connectedtogether in any suitable manner, such as by being adhesively bonded to aconventional spacer frame 24. A gap or chamber 26 is formed between thetwo plies 12, 18. The chamber 26 can be filled with a selectedatmosphere, such as air, or a non-reactive gas such as argon or kryptongas. A solar control coating 30 (or any of the other coatings describedherein) is formed over at least a portion of one of the plies 12, 18,such as, but not limited to, over at least a portion of the No. 2surface 16 or at least a portion of the No. 3 surface 20. Although, thecoating could also be on the No. 1 surface or the No. 4 surface, ifdesired. Examples of insulating glass units are found, for example, inU.S. Pat. Nos. 4,193,236; 4,464,874; 5,088,258; and 5,106,663.

The plies 12, 18 of the transparency 10 can be of the same or differentmaterials. The plies 12, 18 can include any desired material having anydesired characteristics. For example, one or more of the plies 12, 18can be transparent or translucent to visible light. Examples of suitablematerials include, but are not limited to, plastic substrates (such asacrylic polymers, such as polyacrylates; polyalkylmethacrylates, such aspolymethylmethacrylates, polyethylmethacrylates,polypropylmethacrylates, and the like; polyurethanes; polycarbonates;polyalkylterephthalates, such as polyethyleneterephthalate (PET),polypropyleneterephthalates, polybutyleneterephthalates, and the like;polysiloxane-containing polymers; or copolymers of any monomers forpreparing these, or any mixtures thereof); ceramic substrates; glasssubstrates; or mixtures or combinations thereof. For example, one ormore of the plies 12, 18 can include conventional soda-lime-silicateglass, borosilicate glass, or leaded glass. The glass can be clearglass. By “clear glass” is meant non-tinted or non-colored glass.Alternatively, the glass can be tinted or otherwise colored glass. Theglass can be annealed or heat-treated glass. The glass can be of anytype, such as conventional float glass, and can be of any compositionhaving any optical properties, e.g., any value of visible transmission,ultraviolet transmission, infrared transmission, and/or total solarenergy transmission.

The first and second plies 12, 18 can each be, for example, clear floatglass or can be tinted or colored glass or one ply 12, 18 can be clearglass and the other ply 12, 18 colored glass. Although not limiting tothe invention, examples of glass suitable for the first ply 12 and/orsecond ply 18 are described in U.S. Pat. Nos. 4,746,347; 4,792,536;5,030,593; 5,030,594; 5,240,886; 5,385,872; and 5,393,593. The first andsecond plies 12, 18 can be of any desired dimensions, e.g., length,width, shape, or thickness. In one exemplary automotive transparency,the first and second plies can each be 1 mm to 10 mm thick, such as 1 mmto 8 mm thick, such as 2 mm to 8 mm, such as 3 mm to 7 mm, such as 5 mmto 7 mm, such as 6 mm thick. Non-limiting examples of glass that can beused are described above.

In one aspect, a solar control coating 30 is deposited over at least aportion of at least one major surface of one of the glass plies 12, 18.In the example shown in FIG. 2, the coating 30 is formed over at least aportion of the inner surface 16 of the outboard glass ply 12. The solarcontrol coating 30 can block, absorb, or filter selected portions of thesolar spectrum, such as, but not limited to, the IR, UV, and/or visiblespectrums.

The solar control coating 30 can be deposited by any conventionalmethod, such as, but not limited to, conventional chemical vapordeposition (CVD) and/or physical vapor deposition (PVD) methods.Examples of CVD processes include spray pyrolysis. Examples of PVDprocesses include electron beam evaporation and vacuum sputtering (suchas magnetron sputter vapor deposition (MSVD)). Other coating methodscould also be used, such as, but not limited to, sol-gel deposition. Inone non-limiting embodiment, the coating 30 can be deposited by MSVD.Examples of MSVD coating devices and methods will be well understood byone of ordinary skill in the art and are described, for example, in U.S.Pat. Nos. 4,379,040; 4,861,669; 4,898,789; 4,898,790; 4,900,633;4,920,006; 4,938,857; 5,328,768; and 5,492,750.

‘U.S. Pat. No. 9,604,875 describes transparencies incorporatingsubcritical metallic layers, such as a transparency incorporating twocontinuous silver layers and a subcritical silver layer. Commercialproducts including tempered and non-tempered versions of the articledescribed below, with tempered product (e.g., SOLARBAN® 90 VT) requiringthicker primer layers, as compared to primer layer thickness of thenon-tempered product (e.g., SOLARBAN® 90) and, with the exception of thesubcritical (discontinuous) silver layer, which cannot be increased inthickness without changing its unique optical properties, thickness ofone or more continuous silver layers can be increased and thicknesses ofone or more primer layers is increased in the tempered product ascompared to the non-tempered product. In one aspect, thickness of one ormore of the flash annealed primer layers is between the thickness of thenon-tempered product and the tempered product, for example where one ormore primer layers has a thickness ranging from the thickness of aprimer layer in the non-tempered product plus 20% to 80% of thethickness difference between the primer layer thicknesses of thetempered product minus the primer layer thicknesses of the non-temperedproducts.

An exemplary non-limiting solar control coating 130 having a subcriticalmetallic layer is shown in FIG. 3. This exemplary coating 130 includes abase layer or first dielectric layer 140 deposited over at least aportion of a major surface of a substrate (e.g., the No. 2 surface 116of the first ply 112). The first dielectric layer 140 can be a singlelayer or can comprise more than one film of antireflective materialsand/or dielectric materials, such as, but not limited to, metal oxides,oxides of metal alloys, nitrides, oxynitrides, or mixtures thereof. Thefirst dielectric layer 140 can be transparent to visible light. Examplesof suitable metal oxides for the first dielectric layer 140 includeoxides of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead,indium, tin, and mixtures thereof. These metal oxides can have smallamounts of other materials, such as manganese in bismuth oxide, tin inindium oxide, etc. Additionally, oxides of metal alloys or metalmixtures can be used, such as oxides containing zinc and tin (e.g., zincstannate, defined below), oxides of indium-tin alloys, silicon nitrides,silicon aluminum nitrides, or aluminum nitrides. Further, doped metaloxides, such as antimony, or indium doped tin oxides or nickel or borondoped silicon oxides, can be used. The first dielectric layer 140 can bea substantially single phase film, such as a metal alloy oxide film,e.g., zinc stannate, or can be a mixture of phases composed of zinc andtin oxides or can be composed of a plurality of films.

For example, the first dielectric layer 140 (whether a single film ormultiple film layer) can have a thickness in the range of 100 Å to 600Å, such as 200 Å to 500 Å, such as 250 Å to 350 Å, such as 250 Å to 310Å, such as 280 Å to 310 Å, such as 300 Å to 330 Å, such as 310 Å to 330Å.

The first dielectric layer 140 can comprise a multi-film structurehaving a first film 142, e.g., a metal alloy oxide film, deposited overat least a portion of a substrate (such as the inner major surface 116of the first ply 112) and a second film 144, e.g., a metal oxide oroxide mixture film, deposited over the first metal alloy oxide film 142.In one non-limiting embodiment, the first film 142 can be a zinc/tinalloy oxide. By “zinc/tin alloy oxide” is meant both true alloys andalso mixtures of the oxides. The zinc/tin alloy oxide can be thatobtained from magnetron sputtering vacuum deposition from a cathode ofzinc and tin. One non-limiting cathode can comprise zinc and tin inproportions of 5 wt. % to 95 wt. % zinc and 95 wt. % to 5 wt. % tin,such as 10 wt. % to 90 wt. % zinc and 90 wt. % to 10 wt. % tin. However,other ratios of zinc to tin could also be used. One suitable metal alloyoxide that can be present in the first film 142 is zinc stannate. By“zinc stannate” is meant a composition of Zn_(x)Sn_(1-X)O_(2-X)(Formula 1) where “x” varies in the range of greater than 0 to lessthan 1. For instance, “x” can be greater than 0 and can be any fractionor decimal between greater than 0 to less than 1. For example, wherex=2/3, Formula 1 is Zn_(2/3)Sn_(1/3)O_(4/3), which is more commonlydescribed as “Zn₂SnO₄”. A zinc stannate-containing film has one or moreof the forms of Formula 1 in a predominant amount in the film.

The second film 144 can be a metal oxide film, such as zinc oxide. Thezinc oxide film can be deposited from a zinc cathode that includes othermaterials to improve the sputtering characteristics of the cathode. Forexample, the zinc cathode can include a small amount (e.g., up to 10 wt.%, such as up to 5 wt. %) of tin to improve sputtering. In which case,the resultant zinc oxide film would include a small percentage of tinoxide, e.g., up to 10 wt. % tin oxide, e.g., up to 5 wt. % tin oxide. Acoating layer deposited from a zinc cathode having up to 10 wt. % tin(added to enhance the conductivity of the cathode) is referred to hereinas “a zinc oxide film” even though a small amount of tin may be present.The small amount of tin in the cathode (e.g., less than or equal to 10wt. %, such as less than or equal to 5 wt. %) is believed to form tinoxide in the predominantly zinc oxide second film 144.

For example, the first film 142 can be zinc stannate and the second film144 can be zinc oxide (for example, 90 wt. % zinc oxide and 10 wt. % tinoxide). For example, the first film 142 can comprise zinc stannatehaving a thickness in the range of 50 Å to 600 Å, such as 50 Å to 500 Å,such as 75 Å to 350 Å, such as 100 Å to 250 Å, such as 150 Å to 250 Å,such as 195 Å to 250 Å, such as 200 Å to 250 Å, such as 200 Å to 220 Å.

The second film 144 can comprise zinc oxide having a thickness in therange of 50 Å to 200 Å, such as 75 Å to 200 Å, such as 100 Å to 150 Å,such as 100 Å to no A.

A first heat and/or radiation reflective metallic layer 146 can bedeposited over the first dielectric layer 140. The first reflectivelayer 146 can include a reflective metal, such as, but not limited to,metallic gold, copper, palladium, aluminum, silver, or mixtures, alloys,or combinations thereof. In one embodiment, the first reflective layer146 comprises a metallic silver layer having a thickness in the range of50 Å to 300 Å, e.g., 50 Å to 250 Å, e.g., 50 Å to 200 Å, such as 70 Å to200 Å, such as 100 Å to 200 Å, such as 125 Å to 200 Å, such as 150 Å to185 Å. The first metallic layer 146 is a continuous layer. By“continuous layer” is meant that the coating forms a continuous film ofthe material and not isolated coating regions.

A first primer layer 148 is located over the first reflective layer 146.The first primer layer 148 can be a single film or a multiple filmlayer. The first primer layer 148 can include an oxygen-capturingmaterial that can be sacrificial during the deposition process toprevent degradation or oxidation of the first reflective layer 146during the sputtering process or subsequent heating processes. The firstprimer layer 148 can also absorb at least a portion of electromagneticradiation, such as visible light, passing through the coating 130.Examples of materials useful for the first primer layer 148 includetitanium, silicon, silicon dioxide, silicon nitride, silicon oxynitride,nickel-chrome alloys (such as Inconel), zirconium, aluminum, alloys ofsilicon and aluminum, alloys containing cobalt and chromium (e.g.,Stellite®), and mixtures thereof. For example, the first primer layer148 can be titanium and can have a thickness in the range of 5 Å to 50Å, e.g., 10 Å to 40 Å, e.g., 20 Å to 40 Å, e.g., 20 Å to 35 Å.

A second dielectric layer 150 is located over the first reflective layer146 (e.g., over the first primer layer 148). The second dielectric layer150 can comprise one or more metal oxide or metal alloy oxide-containingfilms, such as those described above with respect to the firstdielectric layer 140. For example, the second dielectric layer 150 caninclude a first metal oxide film 152, e.g., a zinc oxide film, depositedover the first primer film 148 and a second metal alloy oxide film 154,e.g., a zinc stannate (Zn₂SnO₄) film, deposited over the first zincoxide film 152. An optional third metal oxide film 156, e.g., anotherzinc oxide layer, can be deposited over the zinc stannate layer.

The second dielectric layer 150 can have a total thickness (e.g., thecombined thicknesses of the layers) is in the range of 50 Å to 1000 Å,e.g., 50 Å to 500 Å, e.g., 100 Å to 370 Å, e.g., 100 Å to 300 Å, e.g.,100 Å to 200 Å, e.g., 150 Å to 200 Å, e.g., 180 Å to 190 Å.

For example, for a multi-film layer, the zinc oxide film 152 (andoptional second zinc oxide film 156, if present) can have a thickness inthe range of 10 Å to 200 Å, e.g., 50 Å to 200 Å, e.g., 60 Å to 150 Å,e.g., 70 Å to 85 Å. The metal alloy oxide layer (zinc stannate) 54 canhave a thickness in the range of 50 Å to 800 Å, e.g., 50 Å to 500 Å,e.g., 100 Å to 300 Å, e.g., 110 Å to 235 Å, e.g., 110 Å to 120 Å.

A subcritical thickness (discontinuous) second metallic layer 158 islocated over the second dielectric layer 150 (e.g., over the second zincoxide film 156, if present, or over the zinc stannate film 154 if not).The metallic material, such as, but not limited to, metallic gold,copper, palladium, aluminum, silver, or mixtures, alloys, orcombinations thereof, is applied at a subcritical thickness such thatisolated regions or islands of the material are formed rather than acontinuous layer of the material. For silver, it has been determinedthat the critical thickness is less than 50 Å, such as less than 40 Å,such as less than 30 Å, such as less than 25 Å. For silver, thetransition between a continuous layer and a subcritical layer occurs inthe range of 25 Å to 50 Å. It is estimated that copper, gold, andpalladium would exhibit similar subcritical behavior in this range. Thesecond metallic layer 158 can include any one or more of the materialsdescribed above with respect to the first reflective layer 146 but thesematerials are not present as a continuous film. In one non-limitingembodiment, the second layer 158 comprises islanded silver with theislands having an effective thickness in the range of 1 Å to 70 Å, e.g.,10 Å to 40 Å, e.g., 10 Å to 35 Å, e.g., 10 Å to 30 Å, e.g., 15 Å to 30Å, e.g., 20 Å to 30 Å, e.g., 25 Å to 30 Å. The subcritical metalliclayer 158 absorbs electromagnetic radiation according to the PlasmonResonance Theory. This absorption depends at least partly on theboundary conditions at the interface of the metallic islands. Thesubcritical metallic layer 158 is not an infrared reflecting layer, likethe first metallic layer 146. The subcritical silver layer 158 is not acontinuous layer. It is estimated that for silver, the metallic islandsor balls of silver metal deposited below the subcritical thickness canhave a height of about 2 nm to 7 nm, such as 5 nm to 7 nm. It isestimated that if the subcritical silver layer could be spread outuniformly, it would have a thickness of about 1.1 nm. It is estimatedthat optically, the discontinuous metal layer behaves as an effectivelayer thickness of 2.6 nm. Depositing the discontinuous metallic layerover zinc stannate rather than zinc oxide appears to increase thevisible light absorbance of the coating, e.g., of the discontinuousmetallic layer.

The thickness values associated with the “subcritical” layers are an“effective thickness”. The effective thickness can be calculated basedon a reference coating speed that is slower than the actual coatingspeed of the commercial coater. For example, a silver layer is appliedonto a substrate at the same coating rate as a commercial coater but ata reduced line speed (reference coating speed) compared to thecommercial coater. The thickness of the coating deposited at thereference coating speed is measured and then the “effective thickness”for a coating deposited at the same coating rate but at the faster linespeed of the commercial costar is extrapolated. For example, if aparticular coating rate provides a silver coating of 25 nm at referencecoating speed that is one-tenth the line speed of the commercial coater,then the “effective thickness” of the silver layer at the same coatingrate but at the commercial costar line speed (i.e., ten time faster thanthe reference coating run) is extrapolated to be 2.5 nm (i.e., one tenththe thickness). However, as will be appreciated, the silver layer atthis effective thickness (below the subcritical thickness) would not bea continuous layer but rather would be a discontinuous layer havingdiscontinuous regions of silver material. Another way to adjust thethickness of the subcritical silver layer is to decrease the powerapplied to the cathode depositing that layer. For example, the coatercould be set up with power supplied to the cathodes to provide knowncoating thicknesses. The power to the cathode for the subcritical silverlayer could then be reduced and the subcritical silver layer thicknessextrapolated based on the reduced power level. Or, a series of samplescould be generated at different power levels until a desired L*, a*, andb* is achieved

A second primer layer 160 can be deposited over the second metalliclayer 158. The second primer layer 160 can be as described above withrespect to the first primer layer 148. In one example, the second primerlayer can be titanium or a nickel-chromium alloy (such as Inconel)having a thickness in the range of 5 Å to 50 Å, e.g., 10 Å to 25 Å,e.g., 15 Å to 25 Å, e.g., 15 Å to 22 Å. Since the absorbance of thesubcritical material depends at least partly on the boundary conditions,different primers (e.g., having different refractive indices) canprovide the coating with different absorbance spectra and, hence, withdifferent colors.

A third dielectric layer 162 can be deposited over the second metalliclayer 158 (e.g., over the second primer film 160). The third dielectriclayer 162 can also include one or more metal oxide or metal alloyoxide-containing layers, such as discussed above with respect to thefirst and second dielectric layers 140, 150. In one example, the thirddielectric layer 162 is a multi-film layer similar to the seconddielectric layer 150. For example, the third dielectric layer 162 caninclude a first metal oxide layer 164, e.g., a zinc oxide layer, asecond metal alloy oxide-containing layer 166, e.g., a zinc stannatelayer deposited over the zinc oxide layer 164, and an optional thirdmetal oxide layer 168, e.g., another zinc oxide layer, deposited overthe zinc stannate layer 166. In one example, both of the zinc oxidelayers 164, 168 are present and each has a thickness in the range of 50Å to 200 Å, such as 75 Å to 150 Å, such as 80 Å to 150 Å, such as 95 Åto 120 Å. The metal alloy oxide layer 166 can have a thickness in therange of 100 Å to 800 Å, e.g., 200 Å to 700 Å, e.g., 300 Å to 600 Å,e.g., 380 Å to 500 Å, e.g., 380 Å to 450 Å.

In one example, the total thickness of the third dielectric layer 162(e.g., the combined thicknesses of the zinc oxide and zinc stannatelayers) is in the range of 200 Å to 1000 Å, e.g., 400 Å to 900 Å, e.g.,500 Å to 900 Å, e.g., 650 Å to 800 Å, e.g., 690 Å to 720 Å.

A third heat and/or radiation reflective metallic layer 170 is depositedover the third dielectric layer 162. The third reflective layer 170 canbe of any of the materials discussed above with respect to the firstreflective layer. In one non-limiting example, the third reflectivelayer 170 includes silver and has a thickness in the range of 25 Å to300 Å, e.g., 50 Å to 300 Å, e.g., 50 Å to 200 Å, such as 70 Å to 151 Å,such as 100 Å to 150 Å, such as 137 Å to 150 Å. The third metallic layeris a continuous layer.

A third primer layer 172 is located over the third reflective layer 170.The third primer layer 172 can be as described above with respect to thefirst or second primer layers. In one non-limiting example, the thirdprimer layer is titanium and has a thickness in the range of 5 Å to 50Å, e.g., 10 Å to 33 Å, e.g., 20 Å to 30 Å.

A fourth dielectric layer 174 is located over the third reflective layer(e.g., over the third primer layer 172). The fourth dielectric layer 174can be comprised of one or more metal oxide or metal alloyoxide-containing layers, such as those discussed above with respect tothe first, second, or third dielectric layers 140, 150, 162. In onenon-limiting example, the fourth dielectric layer 174 is a multi-filmlayer having a first metal oxide layer 176, e.g., a zinc oxide layer,deposited over the third primer film 172, and a second metal alloy oxidelayer 178, e.g., a zinc stannate layer, deposited over the zinc oxidelayer 176. In one non-limiting embodiment, the zinc oxide layer 176 canhave a thickness in the range of 25 Å to 200 Å, such as 50 Å to 150 Å,such as 60 Å to 100 Å, such as 80 Å to 90 Å. The zinc stannate layer 178can have a thickness in the range of 25 Å to 500 Å, e.g., 50 Å to 500 Å,e.g., 100 Å to 400 Å, e.g., 150 Å to 300 Å, e.g., 150 Å to 200 Å, e.g.,170 Å to 190 Å.

In one non-limiting example, the total thickness of the fourthdielectric layer 174 (e.g., the combined thicknesses of the zinc oxideand zinc stannate layers) is in the range of 100 Å to 800 Å, e.g., 200 Åto 600 Å, e.g., 250 Å to 400 Å, e.g., 250 Å to 270 Å.

An overcoat 180 can be located over the fourth dielectric layer 174. Theovercoat 180 can help protect the underlying coating layers frommechanical and chemical attack. The overcoat 180 can be, for example, ametal oxide or metal nitride layer. For example, the overcoat 180 can betitania having a thickness in the range of 10 Å to 100 Å, such as 20 Åto 80 Å, such as 30 Å to 50 Å, such as 30 Å to 45 Å. Other materialsuseful for the overcoat include other oxides, such as silica, alumina,or a mixture of silica and alumina.

In one non-limiting embodiment, the transparency 10 has a percentreflectance (% R) of visible light from the No. 1 surface in the rangeof 5% to 50%, such as 20% to 40%, such as 25% to 30%. The transparency10 has a visible light transmittance of greater than 20%, such asgreater than 30%, such as greater than 40%. The transparency has a solarheat gain coefficient (SHGC) of less than 0.3, such as less than 0.27,such as less than 0.25.

The ply coated with the coating 130 can be tempered or heat treatedwithout adversely impacting upon the performance characteristics of thearticle or producing haze. Also, the article of the invention has aneutral or moderate reflected color, such as blue or blue-green, in bothreflection and transmission.

The lack of haze upon heating is believed due to the islanded structureof the discontinuous intermediate metallic layer. A side view of asubcritical metallic layer 190 having discontinuous coating regions 191formed on a dielectric layer 192 and covered by a primer layer 194 isshown in FIG. 4. The subcritical metal thickness causes the metalmaterial to form discontinuous regions or islands of metal or metaloxide on the dielectric layer 192. When the primer layer is applied overthe subcritical metal layer, the material of the primer layer covers theislands and can also extend into the gaps between adjacent islands ofthe subcritical metal and contact the underlying layer 192.

The coating 130 provides various advantages over known coatings. Forexample, the subcritical metallic layer increases the visible lightabsorbance of the coating, making the coated article darker. Thecombination of the subcritical metallic layer with selected thicknessesof the dielectric layers can provide the coated article with anasymmetrical reflectance. The color of the article can be tuned intransmission by changing the primer(s) used in the coating. Also, thecoating of the invention is able to be heat treated without introducinghaze.

It is to be understood that the previously described coating 130 is notlimiting to the invention. For example, the subcritical metallic layeris not required to be the second (intermediate) metallic layer in thestack. The subcritical metallic layer could be placed anywhere in thecoating stack. Also, for coating stacks having a plurality of metalliccoating layers, more than one of the metallic layers could be asubcritical metallic layer.

While the above example included two continuous metal layers and onediscontinuous metal layer, it is to be understood that this is just onenon-limiting example. In the broad practice of the invention, thecoating of the invention could include multiple continuous metalliclayers and multiple discontinuous metallic layers. For example, a coatedarticle could include a single subcritical metallic layer locatedbetween two dielectric layers. Or, the coating could include 3 or moremetallic layers, such as 4 or more metallic layers, such as 5 or moremetallic layers, such as 6 or more metallic layers, with at least one ofthe metallic layers being a subcritical metallic layer. Variations ofthe coating 130 are further described in U.S. Pat. No. 9,604,875.

Articles having two or more silver coating layers in a solar controlcoating are broadly-known. In one example, a solar controltransparencies include a substrate, and over the substrate, from one tofour iterations of a layer comprising, in order in a direction away froma substrate, a dielectric layer, a metallic layer, and a primer layer,e.g., as disclosed in U.S. Pat. No. 7,910,229, describing a coating withthree silver layers, or United States Patent Application Publication No.20110117300, describing a high solar heat gain coefficient coatinghaving two silver layers. One or more metallic layers may bediscontinuous, for example as described below.

Commercial products including tempered and non-tempered versions of thearticles described below, with tempered product (e.g., SOLARGATE® 460VT,or SOLARBAN® 70 VT) requiring thicker primer layers, as compared toprimer layer thickness of the non-tempered product (e.g., SOLARGATE®460, or SOLARBAN® 70 XL), and, with the exception of any subcritical(discontinuous) silver layer, which cannot be increased in thicknesswithout changing its unique optical properties, thickness of one or morecontinuous silver layers can be increased and thicknesses of one or moreprimer layers is increased in the tempered product as compared to thenon-tempered product. In one aspect, thickness of one or more of theflash annealed primer layers is between the thickness of thenon-tempered product and the tempered product, for example where one ormore primer layers has a thickness ranging from the thickness of aprimer layer in the non-tempered product plus 20% to 80%, or 30% to 70%,of the thickness difference between the primer layer thicknesses in thetempered product minus the primer layer thicknesses in the non-temperedproducts.

As shown in FIG. 5, an exemplary coating 130 includes a base layer orfirst dielectric layer 240 deposited over at least a portion of a majorsurface of a substrate (e.g., the No. 2 surface 216 of the first ply212). The first dielectric layer 240 can be a single layer or cancomprise more than one film of antireflective materials and/ordielectric materials, such as, but not limited to, metal oxides, oxidesof metal alloys, nitrides, oxynitrides, or mixtures thereof. The firstdielectric layer 240 can be transparent to visible light. Examples ofsuitable metal oxides for the first dielectric layer 240 include oxidesof titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium,tin, and mixtures thereof. These metal oxides can have small amounts ofother materials, such as manganese in bismuth oxide, tin in indiumoxide, etc. Additionally, oxides of metal alloys or metal mixtures canbe used, such as oxides containing zinc and tin (e.g., zinc stannate,defined below), oxides of indium-tin alloys, silicon nitrides, siliconaluminum nitrides, or aluminum nitrides. Further, doped metal oxides,such as antimony or indium doped tin oxides or nickel or boron dopedsilicon oxides, can be used. The first dielectric layer 240 can be asubstantially single phase film, such as a metal alloy oxide film, e.g.,zinc stannate, or can be a mixture of phases composed of zinc and tinoxides or can be composed of a plurality of films.

For example, the first dielectric layer 240 (whether a single film ormultiple film layer) can have a thickness in the range of 100 Å to 600Å, such as 100 Å to 500 Å, such as 100 Å to 350 Å, such as 150 Å to 300Å, such as 200 Å to 250 Å, such as 210 Å to 220 Å.

The first dielectric layer 240 can comprise a multi-film structurehaving a first film 142, e.g., a metal alloy oxide film, deposited overat least a portion of a substrate (such as the inner major surface 216of the first ply 212) and a second film 244, e.g., a metal oxide oroxide mixture film, deposited over the first metal alloy oxide film 242.In one non-limiting embodiment, the first film 242 can be zinc stannate.

For example, the first film 242 can be zinc stannate and the second film244 can be zinc oxide (for example, 90 wt. % zinc oxide and 10 wt. % tinoxide). For example, the first film 242 can comprise zinc stannatehaving a thickness in the range of 50 Å to 600 Å, such as 50 Å to 500 Å,such as 75 Å to 350 Å, such as 100 Å to 250 Å, such as 100 Å to 200 Å,such as 100 Å to 150 Å, such as 140 Å to 150 Å.

The second film 244 can comprise zinc oxide having a thickness in therange of 50 Å to 200 Å, such as 50 Å to 150 Å, such as 70 Å to 180 Å.

In another exemplary coating, the first dielectric layer 240 comprises afirst layer comprising zinc stannate, a second layer comprising zincoxide, a third layer comprising zinc stannate, and a fourth layercomprising zinc oxide, wherein the first dielectric layer has athickness in the range of 44 nm to 48 nm, the first layer and thirdlayer each have a thickness in the range of 16 nm to 17 nm, and thesecond layer and fourth layer each have a thickness in the range of 6 nmto 8 nm.

A first heat and/or radiation reflective metallic layer 246 can bedeposited over the first dielectric layer 240. The first reflectivelayer 246 can include a reflective metal, such as, but not limited to,metallic gold, copper, palladium, silver, or mixtures, alloys, orcombinations thereof. In one embodiment, the first reflective layer 246comprises a metallic silver layer having a thickness in the range of 25Å to 300 Å, e.g., 50 Å to 300 Å, e.g., 50 Å to 250 Å, e.g., 50 Å to 200Å, such as 70 Å to 200 Å, such as 100 Å to 200 Å, such as 120 Å to 180Å.

A first primer layer 248 is located over the first reflective layer 246.The first primer layer 148 can be a single film or a multiple filmlayer. The first primer layer 248 can include an oxygen-capturingmaterial that can be sacrificial during the deposition process toprevent degradation or oxidation of the first reflective layer 246during the sputtering process or subsequent heating processes. The firstprimer layer 248 can also absorb at least a portion of electromagneticradiation, such as visible light, passing through the coating 230.Examples of materials useful for the first primer layer 248 includetitanium, Inconel, Stellite®, and mixtures thereof. For example, thefirst primer layer 248 can have a thickness in the range of 5 Å to 50 Å,e.g., 10 Å to 40 Å, e.g., 20 Å to 40 Å, e.g., 20 Å to 30 Å. In oneexample, the first primer 148 is titanium.

An optional outer dielectric layer 274 is located over the outermostiteration of the primer film 248. The outer dielectric layer 274 can becomprised of one or more metal oxide or metal alloy oxide-containinglayers, such as those discussed above with respect to the firstdielectric layers 240. In one non-limiting example, the outer dielectriclayer 274 is a multi-film layer having a first metal oxide layer 276,e.g., a zinc oxide layer, deposited over the third primer film 272, anda second metal alloy oxide layer 278, e.g., a zinc stannate layer,deposited over the zinc oxide layer 276. In one non-limiting embodiment,the zinc oxide layer 276 can have a thickness in the range of 25 Å to200 Å, such as 50 Å to 150 Å, such as 60 Å to 100 Å, such as 70 Å to 90Å. The zinc stannate layer 278 can have a thickness in the range of 25 Åto 500 Å, e.g., 50 Å to 500 Å, e.g., 100 Å to 400 Å, e.g., 150 Å to 300Å, e.g., 150 Å to 200 Å, e.g., 170 Å to 200 Å.

In aspects, one, two, three, or four additional iterations of theassembly 249 including the dielectric layer 240, the heat and/orradiation reflective metallic layer 246, and the primer layer 248, maybe deposited over the primer layer and beneath the outer dielectriclayer 274. In one aspect, where there are two or more iterations ofassembly 249, one or more of the heat and/or radiation reflectivemetallic layers 246, is subcritical, for example and without limitation,as shown in FIG. 4.

In one non-limiting example, the total thickness of the outer dielectriclayer 274 (e.g., the combined thicknesses of the zinc oxide and zincstannate layers) is in the range of 100 Å to 800 Å, e.g., 200 Å to 600Å, e.g., 250 Å to 400 Å, e.g., 250 Å to 270 Å.

An overcoat 280 can be located over the fourth dielectric layer 274. Theovercoat 280 can help protect the underlying coating layers frommechanical and chemical attack. The overcoat 280 can be, for example, ametal oxide or metal nitride layer. For example, the overcoat 280 can betitania having a thickness in the range of 10 Å to 100 Å, such as 20 Åto 80 Å, such as 30 Å to 50 Å, such as 30 Å to 40 Å.

Another exemplary non-limiting coating 330 is shown in FIG. 6. Thisexemplary coating 330 includes a base layer or first dielectric layer340 deposited over at least a portion of a major surface of a substrate(e.g., the No. 2 surface 16 of the first ply 12). The first dielectriclayer 340 can be similar to the first dielectric layer 40 describedabove. For example, the first dielectric layer 340 can be a single layeror can comprise more than one film of antireflective materials and/ordielectric materials, such as, but not limited to, metal oxides, oxidesof metal alloys, nitrides, oxynitrides, or mixtures thereof. The firstdielectric layer 340 can be transparent to visible light. Examples ofsuitable metal oxides for the first dielectric layer 340 include oxidesof titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium,tin, and mixtures thereof. These metal oxides can have small amounts ofother materials, such as manganese in bismuth oxide, tin in indiumoxide, etc. Additionally, oxides of metal alloys or metal mixtures canbe used, such as oxides containing zinc and tin (e.g., zinc stannate,defined below), oxides of indium-tin alloys, silicon nitrides, siliconaluminum nitrides, or aluminum nitrides. Further, doped metal oxides,such as antimony or indium doped tin oxides or nickel or boron dopedsilicon oxides, can be used. The first dielectric layer 340 can be asubstantially single phase film, such as a metal alloy oxide film, e.g.,zinc stannate, or can be a mixture of phases composed of zinc and tinoxides or can be composed of a plurality of films.

For example, the first dielectric layer 340 (whether a single film ormultiple film layer) can have a thickness in the range of 100 Å to 800Å, such as 100 Å to 600 Å, such as 200 Å to 600 Å, such as 400 Å to 500Å, such as 440 Å to 500 Å.

The first dielectric layer 340 can comprise a multi-film structurehaving a first film 342, e.g., a metal alloy oxide film, deposited overat least a portion of a substrate (such as the inner major surface 16 ofthe first ply 12) and a second film 344, e.g., a metal oxide or oxidemixture film, deposited over the first metal alloy oxide film 342. Inone non-limiting embodiment, the first film 342 can be zinc stannate.

For example, the first film 342 can be zinc stannate and the second film344 can be zinc oxide (for example, 90 wt. % zinc oxide and 10 wt. % tinoxide). For example, the first film 342 can comprise zinc stannatehaving a thickness in the range of 50 Å to 600 Å, such as 50 Å to 500 Å,such as 75 Å to 400 Å, such as 200 Å to 400 Å, such as 300 Å to 400 Å,such as 355 Å to 400 Å.

The second film 344 can comprise zinc oxide having a thickness in therange of 50 Å to 200 Å, such as 50 Å to 150 Å, such as 85 Å to 100 Å.

A first heat and/or radiation reflective metallic layer 346 can bedeposited over the first dielectric layer 340. The first reflectivelayer 346 can include a reflective metal, such as, but not limited to,metallic gold, copper, silver, or mixtures, alloys, or combinationsthereof. In one embodiment, the first reflective layer 346 comprises ametallic silver layer having a thickness in the range of 25 Å to 300 Å,e.g., 50 Å to 300 Å, e.g., 50 Å to 250 Å, e.g., 50 Å to 200 Å, such as70 Å to 200 Å, such as 70 Å to 100 Å, such as 73 Å to 100 Å.

A first primer layer 348 is located over the first reflective layer 346.The first primer layer 348 can be a single film or a multiple filmlayer. The first primer layer 348 can include an oxygen-capturingmaterial that can be sacrificial during the deposition process toprevent degradation or oxidation of the first reflective layer 346during the sputtering process or subsequent heating processes. The firstprimer layer 348 can also absorb at least a portion of electromagneticradiation, such as visible light, passing through the coating 330.Examples of materials useful for the first primer layer 348 includetitanium, Inconel, Stellite®, and mixtures thereof. For example, thefirst primer layer 348 can be a multi-film layer having a first primerfilm 349 and a second primer film 351. The first and second primer films349, 351 are typically of different materials. For example, the firstprimer film 349 can be Inconel having a thickness in the range of 1 Å to10 Å, e.g., 1 Å to 5 Å. The second primer film 351 can be titaniumhaving a thickness in the range of 5 Å to 20 Å, e.g., 10 Å to 15 Å.

A second dielectric layer 350 is located over the first reflective layer346 (e.g., over the first primer layer 348). The second dielectric layer350 can comprise one or more metal oxide or metal alloy oxide-containingfilms, such as those described above with respect to the firstdielectric layer 340. For example, the second dielectric layer 350 caninclude a first metal oxide film 352, e.g., a zinc oxide film, depositedover the first primer film 348 and a second metal alloy oxide film 354,e.g., a zinc stannate (Zn2SnO4) film, deposited over the first zincoxide film 352. An optional third metal oxide film 356, e.g., anotherzinc oxide layer, can be deposited over the zinc stannate layer.

The second dielectric layer 350 can have a total thickness (e.g., thecombined thicknesses of the layers if more than one layer is present) isin the range of 50 Å to 1000 Å, e.g., 50 Å to 800 Å, e.g., 100 Å to 800Å, e.g., 200 Å to 800 Å, e.g., 500 Å to 700 Å, e.g., 650 Å to 700 Å.

For example, for a multi-film layer, the zinc oxide film 352 (andoptional third zinc oxide film 356, if present) can have a thickness inthe range of 10 Å to 200 Å, e.g., 50 Å to 200 Å, e.g., 50 Å to 150 Å,e.g., 50 Å to 75 Å. The metal alloy oxide layer (zinc stannate) 54 canhave a thickness in the range of 50 Å to 800 Å, e.g., 50 Å to 500 Å,e.g., 100 Å to 500 Å, e.g., 400 Å to 500 Å.

A reflective metallic layer 358 is located over the second dielectriclayer 350 (e.g., over the third zinc oxide film 356, if present, or overthe zinc stannate film 354 if not). In one non-limiting embodiment, thesecond reflective layer 358 comprises silver having a thickness in therange of 50 Å to 300 Å, e.g., 100 Å to 200 Å, e.g., 150 Å to 200 Å,e.g., 170 Å to 200 Å.

A second primer layer 372 can be deposited over the second reflectivelayer 358. The second primer layer 372 can be as described above withrespect to the first primer layer 348. For example, the second primerlayer 372 can be a multi-film layer having a first primer film 371 and asecond primer film 373. The first and second primer films 371, 373 aretypically of different materials. For example, the first primer film 371can be Inconel having a thickness in the range of 1 Å to 15 Å, e.g., 5 Åto 10 Å. The second primer film 373 can be titanium having a thicknessin the range of 5 Å to 20 Å, e.g., 10 Å to 15 Å.

A third dielectric layer 374 can be deposited over the second reflectivelayer 358 (e.g., over the second primer film 372). The third dielectriclayer 374 can also include one or more metal oxide or metal alloyoxide-containing layers, such as discussed above with respect to thefirst and second dielectric layers 340, 350. In one example, the thirddielectric layer 374 is a multi-film layer similar to the seconddielectric layer 350. In one non-limiting example, the third dielectriclayer 374 is a multi-film layer having a first metal oxide layer 376,e.g., a zinc oxide layer, deposited over the second primer layer 372,and a second metal alloy oxide layer 378, e.g., a zinc stannate layer,deposited over the zinc oxide layer 376. In one non-limiting embodiment,the zinc oxide layer 376 can have a thickness in the range of 25 Å to200 Å, such as 50 Å to 150 Å, such as 100 Å to 150 Å. The zinc stannatelayer 378 can have a thickness in the range of 25 Å to 500 Å, e.g., 50 Åto 500 Å, e.g., 100 Å to 400 Å, e.g., 200 Å to 350 Å, e.g., 300 Å to 350Å, e.g., 320 Å to 350 Å.

In one non-limiting example, the total thickness of the third dielectriclayer 374 (e.g., the combined thicknesses of the zinc oxide and zincstannate layers) is in the range of 100 Å to 800 Å, e.g., 200 Å to 600Å, e.g., 250 Å to 500 Å, e.g., 470 Å to 500 Å.

An overcoat 380 can be located over the third dielectric layer 374. Theovercoat 380 can help protect the underlying coating layers frommechanical and chemical attack. The overcoat 380 can be, for example, ametal oxide or metal nitride layer. For example, the overcoat 380 can betitania having a thickness in the range of 10 Å to 100 Å, such as 20 Åto 80 Å, such as 30 Å to 50 Å, such as 30 Å to 40 Å.

The following Examples illustrate various embodiments of the invention.However, it is to be understood that the invention is not limited tothese specific embodiments.

In one aspect, a coating is flashed in a pattern to produce atransmittance and/or reflective pattern in the coating. Patterns incoatings are useful for a variety of reasons, ranging from the aestheticto the functional. For example, a pattern may be produced to make atransparency more visible to wildlife, e.g. to reduce collisions withbirds, to create a desirable aesthetic effect, or to create a partialprivacy screen or a graded density or effect. In another aspect, acoating is patterned to create a pattern of low resistivity, e.g.circuits, in the coating, for example, for use in electro-opticaldevices. In one aspect, the pattern is created by interposing a filteror opaque object or mask, such as a sheet between the flash lamp and thecoating to be flashed.

Referring to FIG. 7, a coating 430, e.g., deposited over at least aportion of a major surface of a substrate (e.g., the No. 2 surface 16 ofthe first ply 12), is flashed as described herein using a flash lamp432. A mask 434 is interposed between the flash lamp 432 and the coating430, producing a shadowing effect, resulting in differential applicationof light in a pattern on the coating 430. Because the shadowing effectcauses different light treatment over the surface of the coating layersof the coating are exposed to different light intensities, and thereforeresult in a pattern of any aspect of layer(s) of the coating affected bythe light, including but not limited to changes in transmittance orreflective color values (e.g. L*a*b* values), transmittance,reflectivity, haze, crystallinity, and/or sheet resistance. The mask 434is shown in an intermediary position between the flash lamp 432 andcoating 430. In practice, the mask can be placed at any position betweenthe lamp 432 and coating 430 effective to produce a desired maskingeffect. Because the light source is incoherent and not necessarily apoint source, in one aspect, it may be preferable to place the mask 434directly on, or as close as possible to the coating 430 to create a moresharply-defined pattern. In another aspect, it may be preferable toplace the mask as shown, or in a position between the coating 430 andthe flash lamp 432 to create a softer, less sharply-defined pattern. Aswould be apparent to one of ordinary skill, the use of a star as themask 434 is merely exemplary, and the mask 434 can have any desiredshape and transparency, and, when less than 100% opaque, the mask 434can have a desired coloring and/or transmittance (acting as a color orneutral density filter) to filter the light from the flash lamp 432,effecting a partial masking of the coating 430. In other aspects,multiple masks may be used. In still other aspects, the mask 434 mayhave a gradient of transmittance (acting as a neutral density gradientfilter) and/or color (acting as a color gradient filter), to produce agradient pattern on the coating 430.

Example 1

ITO-coated glass articles were prepared by MSVD deposition of an ITOlayer onto 3.2 mm thick float glass in argon with varying pressure andpercentages of O₂, to the thickness indicated in FIG. 8. The articleswere flashed at room temperature (˜22° C.) with a single pulse of 500micro seconds and ˜4-5 J/cm². Sheet resistance was measured using a fourpoint probe and results are provided in FIG. 8. Adequate sheetresistance (<30Ω/□), with sheet resistances of less than 20Ω/□ forlayers of over 125 nm. Emissivity for the same coated articles wasevaluated by standard methodology, with the results depicted in FIG. 9,showing that for ITO layers of over 150 nm in thickness, and especiallyin the range of from 250 nm to 350 nm, emissivity changes over two- tofive-fold and is raised to 35Ω/□.

Example 2

ITO-coated articles were prepares essentially as indicated in Example 1,except that the pressure, O₂ percentage and thicknesses were varied asindicated in FIGS. 10A and 10B. The samples were flashed with a ˜500microseconds pulse from a Xenon lamp at ˜4-5 J/cm². Hall measurements(carrier concentration and carrier mobility) were measured by standardmethods. As can be seen in FIGS. 10A and 10B, carrier mobility andconcentration increased after flashing, indicating an overall increasein conductivity, but the greatest increase in carrier concentration wasseen for the ITO deposited at 4 mTorr and 1.5% O₂.

Example 3

ITO-coated articles were prepared essentially as in Example 1, with theexception that all samples had ITO layers of 250 nm thickness, depositedby MSVD in argon at 4 mTorr, with 0%, 1.5%, or 2.5% O₂. Transmission wasmeasured spectrophotometrically, and Normalized absorption wascalculated from transmission and reflection data. Results are shown inFIGS. 11A and 11B. Integrated transmittance is indicated for two samplesets. Samples were flashed with a single pulse of ˜500 microseconds at˜4-5 J/cm². Significant differences are seen in transmittance andnormalized absorption between pre-flashed and flashed samples within thevisible and near infrared spectra for 0% and 1.5% O₂ samples, whilelittle effect is see with 2.5% O₂, indicating that oxygen-deficient ITOis more reactive to flashing.

Example 4

ITO-coated articles were prepares essentially as indicated in Example 1,except that the pressure, O₂ percentage was 3 mTorr and 2.5% O₂, andthicknesses were varied as indicated in FIG. 12. The samples wereflashed with a ˜500 microseconds pulse from a Xenon lamp at ˜4-5 J/cm².Sheet resistance and integrated transmittance were evaluated by standardmethods. As can be seen in FIG. 12, for ITO deposited at 4 mTorr and1.5% O₂, for sheets ranging from 250 nm to greater than 650 nm low sheetresistance and transmittance can be obtained by flash annealing.

Example 5

ITO-coated articles were prepared essentially as described in Example 1,with the exception that the ITO layer thickness was approximately 300nM. Different ITO deposition conditions were used, resulting inabsorption coefficient spectra as indicated in FIG. 13A, determined bystandard methodology. The samples were flashed with a ˜500 microsecondspulse from a Xenon lamp at ˜4-5 J/cm². X-ray diffraction (XRD) traceswere obtained by standard methodology for each sample (FIG. 13B). As canbe seen in FIG. 13A, as the absorption coefficient increases for lightbetween 425 nm and 500 nm, the penetration depth of the light decreases,and a shifting and enhancement of XRD peaks is seen for sample 2, whilea splitting or bifurcating of peaks is seen for sample 3, indicative ofthe formation of two sub-layers from a single ITO layer.

As shown in FIG. 13A, the absorption coefficient of the layer affectsthe penetration depth of the flash. For layers of sufficient thicknessand having sufficiently high absorption coefficients, the depth ofpenetration of the flash into the layer can be modulated such that thelayer is only partially transformed, resulting in a split ITO layerhaving different physical characteristics. In such an instance, the ITOlayer can be bifurcated into a first layer (closer to the flash lamp)that is physically converted by the flash, and a second layer (fartheraway from the flash) that is not. Thus, as shown in FIG. 13B, coatingswith larger absorption coefficient (lower penetration depth) showssplitting. Coatings with intermediate absorption coefficient (andpenetration depth) show shifting of the peaks. Coatings with highestpenetration depth (lowest absorption) exhibit nearly no change in XRDpattern.

Example 6

ITO-coated articles were prepared essentially as described in Example 1,with the exception that the ITO layer thickness was as indicated in FIG.14, and ITO was deposited at 4 mTorr with 1.5% O₂. The samples wereflashed with a ˜500 microseconds pulse from a Xenon lamp at ˜4-5 J/cm².XRD diffraction traces are provided in FIG. 14. As can be seen, allthicknesses exhibited transformation as a result of flashing, but as thethickness of the layer increased, e.g. beyond the effective penetrationdepth of the light pulse for this particular ITO composition,bifurcation of the layer into two physically-different sub-layers isseen with thicknesses over 186 nm. For different ITO and TCOcompositions, and for different flash spectra and intensities,bifurcation is expected to begin at different thicknesses.

Example 7

A 12″×12″ sheet of a MSVD coating product was prepared on monolithicglass essentially as described in United States Patent ApplicationPublication No. 20110117300, with, in order: substrate, a firstdielectric layer (40-55 nm), a reflective layer (5.5-8.5 nm), a primerlayer (0.5-6 nm), a second dielectric layer (15-45 nm), and a protectivelayer of up to 15 nm. These thicknesses are for an annealed product. Itwas found that use of primer thicknesses in this range resulted in hazeand loss of visual quality after flashing. The nominal product describedabove was therefore modified to increase both primer thicknesses by 1kW, to increase both primer thicknesses by 1.5 kW and to decrease topand center oxides by 3 kW, or to increase both primer thicknesses by 2kW and to decrease top and center oxides by 3 kW.

NovaCentrix PulseForge 1300 system was used for flash heating the testsubstrates. The stage was set at a z-height of 13 mm. For the ‘processdevelopment’, 2″×2″ squares of the coated glass were used with thePulseForge set to flash one time in ‘fixed position’ mode. The sheetresistance of these samples was measured before and after flashprocessing via 4-point probe.

The samples submitted for analytical analysis were 4″×4″. The flashparameters used were the set identified as preferred based on the 2″×2″results, but as the piece was larger than the region covered by a singleflash event, the mode was shifted to “once through” with overlap set at2.0 and throughput set at 10 ft/min.

FIG. 15 shows flash conditions used in this assessment. The ‘1 kW’series of samples are all cut from one of the 12×12 s of Sungate 460with the primer increased by 1 kW, the ‘1.SkW’ series of samples are allcut from one of the 12×12 s of Sungate 460 with the primer increased by1.5 kW, and the ‘2 kW’ series of samples are all cut from one of the12×12 s of Sungate 460 with the primer increased by 2 kW. The ‘Norn’series of samples are the cut from a 12×12 of nominal Sungate 460. The‘before flash’ sheet resistances showed slight differences between theversions, with the nominal Sungate 460 before-flash sheet resistivity ofapproximately 3.68 Q/sq. being the highest, the ‘1 kW’ and ‘1.SkW’series showing approximately 3.58 Q/sq. and the ‘2 kW’ series measuringclose to 3.63 Q/sq.

The lowest after-flash sheet resistivity sample from each 12×12 ishighlighted in green. Note that in three of the green highlightedsamples used 640V and 500 μs pulse duration for the flash annealing. Ofthese results, the three lowest after-flash resistances overall involved‘1.5 kW’ pieces under different flash conditions. The 12×12 showing theleast benefit from the flash process was the sample A. “DAM” in the Rsafter flash column is used to indicate a presumption of damage to thecoating as a result of the flash; in these cases it is believed that theflash power, which increases both with increasing voltage and withincreasing duration, was higher than the optimal level.

Based on this result, a 4″×4″ piece of the 1.5 kW material was cut andflashed under the same flash setpoints (using “Once Through” mode, asdescribed above}. Three total 4″×4″ samples were prepared and submittedfor emissivity and SHGC characterization, as follows: Sample A(NOM-4×4), unflashed Sample C, and flashed Sample C. FIGS. 16 and 17 aretables showing the visible color and performance properties, assimulated integrated into insulated glass devices using two lites of 3.2mm clear glass and a 0.5″ air gap, for five different coatings: thethree described 4″×4″ samples, a commercial annealed product, and acommercial tempered version of the annealed product.

As seen in FIG. 15, the lowest after-flash sheet resistivity ishighlighted. Three of the highlighted samples used 640V and 500 μs flashduration, and the three lowest after-flash sheet resistances involved1.5 kW primer pieces. Samples marked “DAM” were presumably damaged as aresult of the flashing above an optimal range. Pieces of the 1.5 kWmaterial were then flashed as above and compared to the nominal productdescribed above and to commercial non-tempered (Sungate 460) andtempered (Sungate 460VT) commercial products using a computer simulationof insulated glass. As can be seen in FIG. 16, the flash-processedsample is very similar in color to the commercial products, with allthree samples showing elevated transmittance as compared to thecommercial products. As can be seen in FIG. 17, the flash-processedsamples showed lower emissivity and higher solar heat gain coefficient.

Example 8

A three silver layer article was prepared essentially as describedabove, e.g. in reference to FIGS. 5 and 6, and corresponding to acommercial SOLARBAN® 70-based coatings, with the goal of determiningwhether a TL* increase could be achieved of a sufficient amount to beable to produce a non-tempered product that would closely match thecommercial tempered product.

A sample set of variations on the non-annealed product was deposited on5 mm clear glass. The sample set variations focused on changes in primerthicknesses and thicknesses of continuous silver layers. A set of fiveflash processing conditions was defined and performed on pieces cut fromeach coating; along with control (unflashed) samples. A set of 102samples was characterized and analyzed, and optical modeling was used todetermine layer thicknesses.

The 17 coating variations were compared to non-tempered (annealed) andtempered (VT) samples as shown in Table 1

TABLE 1 Silver Layer Variation (% increase above nominal) Primer: 0 1 23 221 Annealed 21C 22C 30% 26C 25C 24C 23C 40% 27C 28C 29C 30C 31C 50%35C 34C 33C 32C VT 36C 37C

In Table 1, the 0, 1, 2, 3, and 221 are % increases in each of thecontinuous silver layers. All the samples listed below ‘0’ weredeposited using nominal silver thickness (+0%) to each layer, each ofthe samples under ‘2’ had silver cathode power increase by about 2%. The‘221’ refers to 2% increase to the bottom silver, 2% increase to thecenter silver, and 1% increase to the top silver. For the primers, 5primer thicknesses were used, including annealed-level primer thickness,the VT level, and three intermediate primers with the % s referring tothe fraction of thickness increase from annealed level to VT level. Forexample, sample “29C” was otherwise identical to productionSOLARBAN′70XL except (1) each of the silver layer power levels (andtherefore nominally silver thicknesses) was increased by about 2% and(2) each primer cathode power level was at a setpoint 40% of the wayfrom the annealed power level increasing toward the VT power level.

Each sample was processed under 6 different flash processing conditions,referred to as “−C”, and “−1” through “−5”. The interpretation of thesesuffixes is given in Table 2:

TABLE 2 Voltage Duration Suffix (V) (μ_(s)) Reps Notes −C NA NA NAUnflashed control −1 660 500 2 −2 660 500 1 −3 620 500 1 −4 675 500 1 −5Recipe 19

Recipe 19 refers to a set of flash conditions that was observed toproduce high TL* values. The process uses 19 flashes at generallyincreasing voltage as follows:

TABLE 3 Voltage Duration Flash (V) (μ_(s)) 1 540 500 2 545 500 3 550 5004 555 500 5 560 500 6 560 500 7 560 500 8 560 500 9 565 500 10 567 50011 569 500 12 569 500 13 571 500 14 573 500 15 575 500 16 577 500 17 579500 18 581 500 19 583 500

Using this nomenclature, sample 36C-3 refers to a piece that was cutfrom a coating that was otherwise identical to the baseline SOLARBAN®70XL except that it used VT primer power levels and was then flashed asingle time at 620 V with a duration of 500 μs. The 100+ samples in thisset allow for single variable comparisons under multiple conditions.

Findings include:

-   -   Samples with annealed level primer thicknesses were commonly        damaged by flash processing; some damage/hazing also was        observed in the 30% primer increase samples;    -   Samples with VT level primers were far off in transmitted color        (high in Tb*) if flashed heavily enough to improve        transmissivity;    -   Increases in TL* as high as 2.3 points were produced using        multiple flashes and as high as a 1.4 increase with a single        flash (relative to the production SOLARBAN® 70XL on 5 mm clear        baseline sample);    -   Flash processed samples were more optically similar to annealed        stacks than as VT stacks; and    -   Thinner oxides would be necessary to maintain color;    -   Thicker silver layers would be necessary to maintain color        (largest increase to bottom Ag, smallest increase to top Ag).

FIG. 18 compares TL* values between flash processed samples, SOLARBAN®70 spec, and relevant production coatings. The ‘single flash’ sample was35C-3 (baseline silver thickness, 50% primer intermediacy), and themultiple flash sample was 35C-5. Both of these samples had notablyhigher TL* values than did the SOLARBAN® 70XL on STARPHIRE® sample; itshould be noted that the flashed sample were on 5 mm clear, and an extramm of clear would be expected to further reduce TL* of the flashedsamples by about 0.1.

A number of the samples (27C through 31C, all flash processes) wereassessed using computer modeling and were determined to be amenable tosuch computer-based optimization processes. The samples werecharacterized and the layer move % s were recorded. Table 4 below showsthe suggested layer move % for each layer from all the characterized −Csamples in the 27C-31C (along with the baseline 21C-C sample). “Nominalmove” refers to the % change relative to baseline power levels used foreach sample (numbers were not exactly 1%, 2%, and 3% as the cathodepowers were adjusted in increments of 0.1 kW; actual adjustments usedare listed in the table). “Ti primer 22% over annealed level” indicatesthat these are the 40% primer intermediacy samples; 22% increase isclose to 40% of the way from annealed to the 56% increase needed toreach VT primer thickness. The “suggested move” cells add the nominalmove value to the to the estimated thickness adjustment needed to retaincolor; assuming self-consistent behavior, these numbers should ideallyremain constant even as continuous silver thicknesses change (e.g., ifthe required thickness adjustment at baseline silver thickness is anincrease of 2%, self-consistent behavior would expect the estimatedrequired thickness adjustment after a 2% increase to be 0%. 0%+2% and2%+0% would give the same resulting “Suggested Move” value).

The results indicated a fair degree of self consistency, with thethickness adjustments needed to retain the SOLARBAN® 70XL aestheticvarying within a much smaller range (˜1%) relative to the changesimplemented into the actual silver layers. The final block of numbersshown, “Adjusted ‘Intrinsic’ Move”, normalizes the estimated layerthickness adjustments required by the corresponding layer thicknessadjustment required for the baseline sample. The most significant effectof this is on the center silver, where a 2.2% increase in center silveris estimated to be needed based on the optics. The intent of this bottomset of numbers is to describe a hypothetical move that would adjust astack that is optimized in its as-deposited state to one that isoptimized for a specific flash process (the previous “Suggested Move”number set is optimized to adjust relative to the arbitrarily usedbaseline stack, which can be assumed to be off thickness in severalplaces by modest amounts even while in color).

TABLE 4 Baseline Control samples (unflashed) Layer 21C-C 27C-C 28C-C29C-C 30C-C 31C-C Base 3.4 3.3 3.3 3.6 3 3 Bottom Ag −0.4 −0.1 −1.9 −2−4.4 −3 BC 0 −1.1 −1.1 −0.8 −1 −1.3 Center Ag 2.2 1.1 0.1 −1 −1.8 −1.5TC −0.5 −0.7 −0.1 −0.4 −0.5 −0.4 Top Ag 0.5 0.1 −0.9 −1.9 −2.7 −1.1 Top−2.2 −4.3 −4.3 −4.5 −4.4 −4 Nominal Move (Ti primer 22% over annealedlevel) B Ag 0 0.72 1.45 2.9 1.45 C Ag 0 1.25 1.88 2.5 1.88 T Ag 0 0.951.9 2.86 0.95 Suggested Move AVG B Ag −0.1 −1.18 −0.55 −1.5 −1.55 −0.976C Ag 1.1 1.35 0.88 0.7 0.38 0.882 T Ag 0.1 0.05 0 0.16 −0.15 0.032Adjusted “Intrinsic” Move AVG B Ag 0.3 −0.78 −0.15 −1.1 −1.15 −0.576 CAg −1.1 −0.85 −1.32 −1.5 −1.82 −1.318 T Ag −0.4 −0.45 −0.5 −0.34 −0.65−0.468

From the tables, average ‘intrinsic’ silver layer thickness changerequirement that were calculated were compiled and compared betweenflash processes; the results are shown in FIG. 19. For the unflashedsamples (−C), the suggested moves are thickness reductions. This isinterpreted as the model fitting metallic Ti as excess Ag; in thisinterpretation, it seems possible that some metallic Ti remains in the−3 samples as well (two of the moves are still reductions). The otherflash processes result in similar counterintuitive thickness adjustmentestimates: increase the bottom silver by 2.5-4.5%, the center silver by1.2-2.5%, and the top silver by 0.2-1.2%.

ΔE_(cmc) is a measure of the overall difference between color profilesof two articles. ΔE_(cmc) was determined for sample 35C-3 and forSOLARBAN® 70XL on STARPHIRE® as compared to SOLARBAN® 70VT. FIG. 20shows that the 35C-3 sample is a significantly closer color match to thetempered product than SOLARBAN® 70XL on STARPHIRE®.

Example 9

A four silver layer article, with a single discontinuous (subcritical)silver layer was prepared essentially as described above, e.g. inreference to FIGS. 3 and 4, and corresponding to commercial SOLARBAN®90-based coatings, with the goal of determining whether a TL* increasecould be achieved and useful color profiles could be generated usingsingle flashes, including 670V for 500 μs, 650V for 500 μs, 800V for 200μs, or 500V for 2000 μs, without damage to the article. Although someflash conditions resulted in less-desirable, e.g., high b* (yellowing)CIELAB L*a*b* profiles, transmittance generally increased and the colorprofile was responsive to the flash processing, with a reduction in hazewith increasing primer thicknesses.

The following clauses provide examples of various aspects of thedisclosure:

1. A method of producing a coated transparency, comprising

-   -   a. depositing a stack of thin layers on a transparent substrate,        the stack comprising a first dielectric layer over at least a        portion of the substrate; a first discontinuous metal layer over        at least a portion of the first dielectric layer; and a first        primer layer over at least a portion of the first discontinuous        metal layer; and    -   b. flashing the transparency at a temperature ranging from        10° C. to 50° C. or ranging from 20° C. to 30° C., with a single        flash of non-coherent light in the visible spectrum with an        intensity ranging from 1 J/m² to 7 J/m² for a pulse length of up        to 10 ms, thereby increasing visible light transmittance of the        transparency.        2. The method of clause 1, further comprising depositing either        between the transparent substrate and the first dielectric        layer, or between the first primer layer and the protective        coating: a second dielectric layer; a first continuous metal        layer over at least a portion of the second dielectric layer;        and a second primer layer over at least a portion of the first        continuous metal layer.        3. The method of clause 2, wherein the second dielectric layer,        the first continuous metal layer, and the second primer layer        are deposited between the transparent substrate and the first        dielectric layer.        4. The method of clause 1 or 2, wherein the stack further        comprises a third dielectric layer over at least a portion of        the first or second primer layer; a second continuous metal        layer over at least a portion of the third dielectric layer; and        a third primer layer over at least a portion of the second        continuous metal layer and beneath the protective coating.        5. The method of clause 4, wherein the stack further comprises,        over at least a portion of the first, second or third primer        layer: a fourth dielectric layer; a third continuous metal layer        over at least a portion of the fourth dielectric layer; and a        fourth primer layer over at least a portion of the third        continuous metal layer.        6. The method of clause 5, comprising: the second dielectric        layer over at least a portion of the transparent substrate; the        first continuous metal layer over at least a portion of the        second dielectric layer; the second primer layer over at least a        portion of the first continuous metal layer; the first        dielectric layer over at least a portion of the second primer        layer; the first discontinuous metal layer over at least a        portion of the first dielectric layer; the first primer layer        over at least a portion of the first continuous metal layer; the        third dielectric layer over at least a portion of the first        primer layer; the second continuous metal layer over at least a        portion of the third dielectric layer; the third primer layer        over at least a portion of the second continuous metal layer;        the fourth dielectric layer over at least a portion of the third        primer layer; the third continuous metal layer over at least a        portion of the fourth dielectric layer; the fourth primer layer        over at least a portion of the third continuous metal layer; a        fifth dielectric layer over at least a portion of the fourth        primer layer; and the protective coating over at least a portion        of the fifth dielectric layer,        7. The method of any one of clauses 1-6, wherein a primer layer        has a thickness ranging from 1 nm to 2 nm.        8. The method of any one of clauses 1-7, wherein the visible        light transmittance of the coated transparency is increased by        the flash pulse.        9. The method of any one of clauses 1-7, wherein the sheet        resistance of the transparency is decreased to 2Ω/□ or less        after a single flash pulse.        10. The method of any one of clauses 1-9, wherein the        non-coherent light source is a xenon flash lamp.        11. The method of any one of clauses 1-10, wherein the flash        pulse ranges from 0.2 ms to 2 ms.        12. The method of any one of clauses 1-11, wherein the first        primer comprises metallic titanium, an austenitic        nickel-chromium alloy (e.g. INCONEL®), or a cobalt-chromium        alloy (e.g. STELLITE®).        13. A non-tempered transparency comprising:    -   a. a clear glass substrate of thickness greater than 2.0 mm;    -   b. a first dielectric layer over at least a portion of the glass        substrate;    -   c. a first silver layer over at least a portion of the first        dielectric layer;    -   d. a first titanium layer over at least a portion of the first        silver layer and having a thickness ranging from 1 to 2 nm;    -   e. a second dielectric layer over at least a portion of the        first titanium layer;    -   f. a second silver layer over at least a portion of the second        dielectric layer;    -   g. a second titanium layer over at least a portion of the second        silver layer and having a thickness ranging from 1 to 2 nm; a        first dielectric layer over at least a portion of the glass        substrate;    -   h. a third dielectric layer over at least a portion of the        second titanium layer;    -   i. a third silver layer over at least a portion of the third        dielectric layer;    -   j. a third titanium layer over at least a portion of the third        silver layer and having a thickness ranging from 1 to 2 nm; a        first dielectric layer over at least a portion of the glass        substrate;    -   k. a fourth dielectric layer over at least a portion of the        third titanium layer; and    -   l. a protective coating over at least a portion of the fourth        dielectric layer,        -   wherein the transparency has normal or near normal, e.g.,            within 8° from normal, transmitted aesthetic CIELAB L*a*b*            values of L* ranging from 87 to 89, a* ranging from −3 to            −5, b* ranging from 3 to 5, and/or a ratio of transmittance            to SHGC of greater than 2.2, for example, h the transparency            has normal or near normal, e.g., within 8° from normal,            transmitted aesthetic CIELAB L*a*b* values of L* ranging            from 87 to 89, a* ranging from −3 to −5, and b* ranging from            3 to 5.            14. A method of flash annealing a transparency, the            transparency comprising: a transparent substrate, a first            dielectric layer over at least a portion of the substrate, a            first continuous metal layer over at least a portion of the            first dielectric layer, a first primer layer over at least a            portion of the first metal layer, a second dielectric layer            over at least a portion of the first primer layer, a second            continuous metal layer over at least a portion of the second            dielectric layer, and a second primer over at least a            portion of the second metal layer, comprising, flashing the            transparency at a temperature ranging from 10° C. to 50° C.            or ranging from 20° C. to 30° C., with a flash of            non-coherent light in the visible spectrum with an intensity            ranging from 1 J/cm² to 7 J/cm² for a pulse length of up to            10 ms, thereby increasing visible light transmittance or            decreasing emissivity of the transparency.            15. The method of clause 14, wherein the flashing produces a            transparency having normal or near normal, e.g., within 8°            from normal, transmitted aesthetic CIELAB color values            matching a non-flashed, tempered product.            16. The method of clause 15, wherein the non-flashed,            tempered product is a tempered product having the same layer            structure (that is, the same layers in the same order, but            not necessarily the same thickness).            17. The method of clause 15, wherein the transparency and            the non-flashed, tempered product have the layer structure:    -   a. a glass substrate;    -   b. a first dielectric layer over at least a portion of the glass        substrate;    -   c. a first silver layer over at least a portion of the first        dielectric layer;    -   d. a first primer layer over at least a portion of the first        silver layer;    -   e. a second dielectric layer over at least a portion of the        first primer layer;    -   f. a second silver layer over at least a portion of the second        dielectric layer;    -   g. a second primer layer over at least a portion of the second        silver layer;    -   h. a third dielectric layer over at least a portion of the        second primer layer;    -   i. a third silver layer over at least a portion of the third        dielectric layer;    -   j. a third primer layer over at least a portion of the third        silver layer; and    -   k. a protective coating over at least a portion of the third        primer layer.        18. The method of any one of clauses 14-17, wherein the metal of        the metal layer is silver.        19. The method of clause 18, wherein the transparency and the        non-flashed product have the layer structure:    -   a. a float glass substrate;    -   b. a first dielectric layer over at least a portion of the glass        substrate;    -   c. a first silver layer over at least a portion of the first        dielectric layer;    -   d. a first titanium layer over at least a portion of the first        silver layer and having a thickness ranging from 1 to 2 nm;    -   e. a second dielectric layer over at least a portion of the        first titanium layer;    -   f. a second silver layer over at least a portion of the second        dielectric layer;    -   g. a second titanium layer over at least a portion of the second        silver layer and having a thickness ranging from 1 to 2 nm;    -   h. a third dielectric layer over at least a portion of the        second titanium layer;    -   i. a third silver layer over at least a portion of the third        dielectric layer;    -   j. a third titanium layer over at least a portion of the third        silver layer and having a thickness ranging from 1 to 2 nm; and    -   k. a protective coating over at least a portion of the third        titanium layer, wherein the transparency has a normal or near        normal, e.g., within 8° from normal, transmitted aesthetic        CIELAB L*a*b* value of L* ranging from 87 to 89, a* ranging from        −3 to −5, and b* ranging from 3 to 5.        20. A method of producing a coated substrate comprising a        plurality of metallic layers, comprising:    -   a. depositing a stack of thin layers on a substrate, the stack        comprising a first dielectric layer over at least a portion of        the substrate, a first metal layer over at least a portion of        the first dielectric layer, a first primer over at least a        portion of the first metal layer, a second dielectric layer over        at least a portion of the first primer layer; a second metal        layer over at least a portion of the second dielectric layer;        and a second primer layer over at least a portion of the second        metal layer; and    -   b. flashing the transparency at a temperature ranging from        10° C. to 50° C., or ranging from 20° C. to 30° C., with a        single flash of non-coherent light in the visible spectrum with        an intensity ranging from 1 J/cm² to 10 J/cm² for a pulse length        of up to 10 ms, wherein a mask is placed between the light        source and the stack of thin layers such that at least a portion        of the flash is masked such that light from the flash is        partially blocked by the mask from reaching the stack of thin        layers, and reaches only a portion of the stack of thin layers,        thereby producing a pattern of reflected color, transmitted        color, differential sheet resistance, and/or emissivity in the        stack of thin layers.        21. The method of clause 20, wherein the substrate is a        transparent substrate.

It will be readily appreciated by those skilled in the art thatmodifications may be made to the invention without departing from theconcepts disclosed in the foregoing description. Accordingly, theparticular embodiments described in detail herein are illustrative onlyand are not limiting to the scope of the invention, which is to be giventhe full breadth of the appended claims and any and all equivalentsthereof.

The invention claimed is:
 1. A non-tempered transparency comprising: a.a substrate of thickness greater than 2.0 mm; b. a first dielectriclayer over at least a portion of the substrate; c. a first metalliclayer over at least a portion of the first dielectric layer; d. a firstprimer layer over at least a portion of the first metallic layer andhaving a thickness ranging from 1 to 2 nm; e. a second dielectric layerover at least a portion of the first primer layer; f. a second metalliclayer over at least a portion of the second dielectric layer; g. asecond primer layer over at least a portion of the second metallic layerand having a thickness ranging from 1 to 2 nm; h. a third dielectriclayer over at least a portion of the second primer layer; i. a thirdmetallic layer over at least a portion of the third dielectric layer; j.a third primer layer over at least a portion of the third metallic layerand having a thickness ranging from 1 to 2 nm; k. a fourth dielectriclayer over at least a portion of the third primer layer; and l. anovercoat over at least a portion of the fourth dielectric layer, whereinthe non-tempered transparency has a normal or near normal transmittedaesthetic CIELAB L*a*b* color value of L* ranging from 87 to 89, a*ranging from −3 to −5, and b* ranging from 3 to
 5. 2. The non-temperedtransparency of claim 1, wherein the non-tempered transparency isflashed annealed with a flash of non-coherent light in the visiblespectrum from a source with an intensity ranging from 1 J/cm² to 7 J/m²for a pulse length of above 0 ms and up to 10 ms, thereby increasingvisible light transmittance of the non-tempered transparency.
 3. Thenon-tempered transparency of claim 2, wherein the flash of non-coherentlight comprises more than one flash of non-coherent light.
 4. Thenon-tempered transparency of claim 2, wherein the non-temperedtransparency has a sheet resistance of 2Ω/□ or less after flashing. 5.The non-tempered transparency of claim 2, wherein the first dielectriclayer, second dielectric layer, third dielectric layer, and/or thefourth dielectric layer comprises a sufficient coefficient of absorptionsuch that the flash of non-coherent light does not penetrate through theentire thickness of the first dielectric layer, second dielectric layer,third dielectric layer, and/or the fourth dielectric layer.
 6. Thenon-tempered transparency of claim 1, wherein the first dielectriclayer, the second dielectric layer, the third dielectric layer, and/orthe fourth dielectric layer comprises zinc oxide.
 7. The non-temperedtransparency of claim 1, wherein the non-tempered transparency is anarchitectural transparency.
 8. The non-tempered transparency of claim 1,wherein the first dielectric layer comprises a first film that is ametal alloy oxide film and a second film that is a metal oxide film. 9.The non-tempered transparency of claim 8, wherein the first film of thefirst dielectric layer comprises zinc stannate and the second film ofthe first dielectric layer comprises zinc oxide.
 10. The non-temperedtransparency of claim 1, wherein the first dielectric layer has athickness in the range of 10 nm to 60 nm.
 11. The non-temperedtransparency of claim 1, wherein the first metallic layer, the secondmetallic layer, and/or the third metallic layer comprises silver. 12.The non-tempered transparency of claim 1, wherein the first primerlayer, the second primer layer, and/or the third primer layer comprisestitanium, an austenitic nickel-chromium alloy, or a cobalt-chromiumalloy.
 13. The non-tempered transparency of claim 12, wherein the firstprimer layer, the second primer layer, and/or the third primer layercomprises titanium
 14. The non-tempered transparency of claim 1, whereinthe first metallic layer has a thickness in the range of 5 nm to 30 nm.15. The non-tempered transparency of claim 1, wherein the secondmetallic layer is a discontinuous layer.
 16. The non-temperedtransparency of claim 15, wherein the second metallic layer has aneffective thickness in the range of 1 nm to 7 nm.
 17. The non-temperedtransparency of claim 1, wherein the overcoat comprises titania.
 18. Thenon-tempered transparency of claim 1, wherein the substrate comprisesglass.
 19. The non-tempered transparency of claim 1, wherein thenon-tempered transparency comprises a percent reflectance in the rangeof 5% to 50%, and a solar heat gain coefficient of less than 0.3. 20.The non-tempered transparency of claim 1, wherein the first metalliclayer and the second metallic layer are continuous layers.